Overview
Benefits
Outstanding elongation enabling flexibility for moving and dynamic surfaces
Cures at room temperature with no hot work or vulcanisation
Protects against erosion and corrosive attack
Bonds to natural rubber, nitrile, neoprene, SBR, polyurethane, PVC, steel, copper and concrete
No solvents, no shrinkage during cure
Small or large areas treated in one operation with no joint lines
Applications
Coating of worn sealing surfaces to enhance and maintain sealing performance.
Coating and protection of rubber parts against wear, tear and chemical effects.
Coating rubber surfaces exposed to impact, friction and environmental effects to extend their service life.
Coating of sealing elements to protect them against wear and chemical effects.
Coating of equipment surfaces exposed to wear, corrosion and erosion with a protective elastomer coating.
Specs
| TECHNICAL DATA | ||||
| Mixing ratio (Base : Solidifier) | 3 : 1 by volume | 2.3 : 1 by weight | ||
| Working life | 15 minutes at 20°C (68°F) | |||
| Shelf life | 3 years | |||
| Adhesion (90° Peel) | Grit blasted mild steel: 3,053 kg/m (171 pli) | |||
| Adhesion (180° Peel) *cohesive failure of substrate | Natural rubber: 214 kg/m (12 pli) |
Neoprene: 671 kg/m (38 pli) |
Nitrile: 897 kg/m (50 pli) |
EPDM: 488 kg/m (27 pli) |
| Elongation | 1000% after 24 hour cure at 20°C (68°F) | 1000% after 7 day cure at 20°C (68°F) | ||
| Tear strength | 4,106 kg/m (230 pli) after 7 day cure at 20°C (68°F) | |||
| Tensile strength | 10.34 MPa (1,500 psi) after 7 day cure at 20°C (68°F) | |||
| Shore A hardness | 73 after 7 day cure at 20°C (68°F) | |||
| Abrasion resistance – loss per 1000 cycles | H18 - 400 mm3 dry | H18 - 180 mm3 wet | ||
Curing Times
| CURE TIMES | ||||
| Temperature | 10°C (50°F) | 20°C (68°F) | 30°C (86°F) | 40°C (104°F) |
| Light loading | 24 hours | 12 hours | 9 hours | 6 hours |
| Full mechanical loading | 72 hours | 36 hours | 32 hours | 28 hours |
| Immersion in chemicals | 5 days | 3 days | 2.5 days | 2 days |