Overview
Belzona 1131 is a 100% solids paste-grade repair system with self lubricating properties for creating low-friction surfaces subject to intermittent contact and low specific loads.
This fully machinable product can vve applied without the need for specialist tools and bonds to virtually any surface including steel aluminium, copper, fibreglass laminate, stainless steel, glass, concrete and brass.
Belzona 1131 has a unique microporous structure to trap and hold lubricatin oil, minimising friction at start up, IT alsa reduces risk of seizure in the event of lubrication starvation.
It does not expand, contract or distort during cure and has excellent electrical insulation properties.
This fully machinable product can vve applied without the need for specialist tools and bonds to virtually any surface including steel aluminium, copper, fibreglass laminate, stainless steel, glass, concrete and brass.
Belzona 1131 has a unique microporous structure to trap and hold lubricatin oil, minimising friction at start up, IT alsa reduces risk of seizure in the event of lubrication starvation.
It does not expand, contract or distort during cure and has excellent electrical insulation properties.
Benefits
Fast Curing
Rapid return to service after application
Excellent Adhesion
Bonds strongly to virtually any rigid surface
High Mechanical Strength
Engineered to withstand demanding mechanical loads
Self Lubricating
Microporous structure traps oil to minimize friction
Applications
Application Areas
Sleeves
shafts
Bearings
Low-Friction Surfaces
Slideways
Specs
| TECHNICAL DATA | |||
|---|---|---|---|
| Mixing ratio (Base : Solidifier) | 3:1 by volume | 4:1 by weight | |
| Working life | 15 minutes at 25°C (77°F) | ||
| Shelf life | 5 years | ||
| Dry heat resistance | 200°C (392°F) | ||
| Adhesion (tensile shear) | Mild steel 20.8 MPa (3,020 psi) |
||
| Compressive strength | 82.9 Mpa (12,030 psi) at 20°C (68°F) cure | ||
| Volume capacity | 561 cm3 (34.2in3)/1 kg | ||
| Heat distortion temperature | 51°C (124°F) at 20°C (68°F) cure | 88°C (190°F) at 100°C (212°F) cure | |
| Abrasion resistance | H10 - 1022 mm3 wet | CS17 - 61 mm3 dry | |
Curing Times
| CURE TIMES | ||||
|---|---|---|---|---|
| Temperature | 10°C (50°F) | 15°C (59°F) | 20°C (68°F) | 25°C (77°F) |
| No loading or immersion | 3 hours | 2 1/4 hours | 1 3/4 hours | 1 hour |
| Machining and/or light loading | 4 hours | 3 hours | 2 hours | 1 1/2 hours |
| Full mechanical or thermal loading | 2 days | 1 1/2 days | 24 hours | 20 hours |